IEC 60335 Household Appliance Test Equipment , Hotplates Aluminum Vessels

Standard:IEC60335-2-9 Clause 3.1.9.108 Figure 103 And Figure 104Test Object:Hotplates
Test:Moisture ResistanceTest Solution:1% NaCl
Solution Amount:See Table 101Figure 103:Vessel For Testing Hotplates
Figure 104:Vessel For Testing Induction HotplatesName:Aluminum Material Vessels For Testing Hotplate
High Light:IEC 60335 Household Appliance Test Equipment ,  CSA Household Appliance Test Equipment ,  SGS aluminum vessels

Aluminum Material Vessels For Testing Hotplate Or Induction Hotplate IEC 60335

Description:

This device is used to simulate the vessel is placed on the hotplates in normal operation.

Confirm to IEC60335-2-9 clause 3.1.9.108 figure 103 and figure 104, Household and similar electrical appliances-Safety-Part 2-9:Particular requirements for grills, toasters and similar portable cooking appliances.

Technical parameters:

Test objectHotplates
Reference standardIEC 60335-2-9 figure 103 and 104
Testmoisture resistance
Test solution1% NaCl
Solution amountsee table 101

Table 101 Quantity of liquid in the vessel:

Diameter of cooking zone (mm)Quantity of water or oil(L)
≤1100.6
>110 and ≤1451.0
>145 and ≤1801.5
>180 and ≤2202.0
>220 and ≤3003.0

Dimensions:

Diameter of cooking zone mmApproximate dimension
a mmb mmc mm
≤1101101408
>110≤1451451408
>145≤1801801409
>180≤22022012010
>220≤30030010010

Figure 103 – Vessel for testing hotplates

The base of the vessel shall not be convex. The concavity of the base of the vessel shall not exceed 0,05 mm.

Figure 104 – Vessel for testing induction hotplates

The vessel is made of low carbon steel having a maximum carbon content of 0,08 %. It is cylindrical without metallic handles or protrusions. The diameter of the flat area of the base of the vessel shall be at least the diameter of the cooking zone. The base of the vessel shall not be convex. The concavity of the base of the vessel shall not exceed 0,006 d.

Test sample: Hotplates